C18080-R540 C18080-TR08機械性能銅合金

UNI-BS Pb10  Italian standard / UNI 7013-72  SS 5640-15 (Cu Pb10 Sn10), CC495K

UNI-BS Pb15  Italian standard / UNI 7013-72  Cu Pb15 Sn (Cu Sn7 Pb15-C), CC496K

UNI-BS Pb20  Italian standard / UNI 7013-72  Cu Pb20 Sn (Cu Sn5 Pb20-C), CC497K

CAC304 (HBsC4)  Japanese standard, JIS SS 5234 (Cu Zn25 Al 5, SoMsF75), CC762S

CAC402 (BC2)  Japanese standard, JIS Rg7 (Cu Sn7 Zn4 Pb7), CC493K

CAC406 (BC6)  Japanese standard, JIS SS 5204-15 (Cu Sn5 Pb5 Zn5), CC491K

CAC502B (PBC2B2)  Japanese standard, JIS SS 5465-15 (Cu Sn12), CC483K

CAC702B (AlBC2)  Japanese standard, JIS AB-200, C954, Ampco 18

CAC703 (AlBC3)  Japanese standard, JIS SS 5716-15, SS 5716-20 (Cu Al10 Ni5 Fe4

C1020  Japanese standard, JIS Cu-OF, Cu-SF

C1100  Japanese standard, JIS Cu-ETP (E-Cu 58)

預熱和層間溫度一般不應超過150℃。焊接鋁含量為10%∼13%的鋁青銅，厚工件推薦預熱和層間溫度約260℃，焊件宜快速冷卻。采用直流反接，短弧和窄焊道施焊。多層焊時層間必須徹底清渣。

普通性能

紫銅是比較純淨的一種銅，一般可近似認為是純銅，導電性、塑性都較好，但強度、硬度較差一些。紫銅具有優良的導熱性延展性和耐蝕性。紫銅中的微量雜質對銅的導電、導熱性能有嚴重影響。其中鈦、磷、鐵、硅等顯著降低電導率,而鎘、鋅等則影響很小。硫、硒、碲等在銅中的固溶度很小,可與銅生成脆性化合物,對導電性影響不大，但能降低加工塑性。

紫銅在大氣、海水和某些非氧化性酸（鹽酸、稀硫酸）、堿、鹽溶液及多種有機酸（醋酸、檸檬酸）中，有良好的耐蝕性，用于化學工業。另外，紫銅有良好的焊接性，可經冷、熱塑性加工制成各種半成品和成品。20世紀70年代，紫銅的產量超過了其他各類銅合金的總產量。

物理性能