C19720-H KLF4-H銅合金材料/材質保書銅合金

JM 11  Johnson Metall / Own brand name on Swedish standard  SS 5475 (Cu Sn14)

JM 12  Johnson Metall / Own brand name on Swedish standard  SS 5458 (Cu Sn10 Zn2), CC482K

JM 14  Johnson Metall / Own brand name on Swedish standard  Cu Pb20 Sn 5 ,  (Cu Sn5 Pb20-V), CC497K

JM 15  Johnson Metall / Own brand name on Swedish standard  SS 5256 (Cu Zn35 Al1), ~CW710R  (CuZn35Ni2) 

JM18  Johnson Metall / Own brand name on Swedish standard  SS 5234 (Cu Zn25 Al 5, SoMsF75), CC762S

JM 100  Johnson Metall / Own brand name on Swedish standard  SS 5015, SF-Cu, CW024A

NS 16304  Norwegian standard / NS  Cu Sn4 (DIN 17662, W-Nr.2.0116)

NS 16306  Norwegian standard / NS  Cu Sn6, CW452K

NS 16508  Norwegian standard / NS  SS 5465-15 (Cu Sn12), CC483K

NS 16525  Norwegian standard / NS  Rg7 (Cu Sn7 Zn4 Pb7), CC493K

NS 16530  Norwegian standard / NS  SS 5204-15 (Cu Sn5 Pb5 Zn5), CC491K

NS 16540  Norwegian standard / NS  SS 5640-15 (Cu Pb10 Sn10), CC495K

NS 16544  Norwegian standard / NS  Cu Pb20 Sn 5, (Cu Sn5 Pb20-V), CC497K

現在的塑膠模具制造當中已有越來越多開始使用鈹銅模具材料，且出現不斷上升的趨勢，造成這一現象的原因是什麼呢？跟隨小編一起來了解鈹銅在塑料模具上的運用，以及原因。

1.足夠的硬度和強度︰在經過很多次的試驗之後，工程師才能夠找出以及掌握鈹銅合金zui佳的沉澱析出的硬化條件以及zui佳工況還有鈹銅的彌撒特性（這一點是鈹銅合金以正式產品開始應用在市場的前奏）；鈹銅材料應用在塑膠模具之前是需要經過多次輪回的試驗來zui終把zui佳的符合制造以及加工的物理特性和化學成分確定下來；理論與實踐的證明鈹銅的硬度在hrc36-42時能夠達到適用于塑膠模具制造要求的硬度、強度、高的導熱率，機加工簡易方便、模具使用壽命長的特點以及節省開發生產周期等。

2.良好的導熱特性︰鈹銅材料的導熱特性有利于控制塑料加工模具的溫度，也更容易控制成型周期，同時可以保證模具壁溫的均勻性；如果與鋼模相比，鈹銅的成型周期要小的多，模具的平均溫度可降低20%左右，當平均脫摸溫度與模具平均壁溫之間相差較小時（例如在模具零件不易被冷卻的情況下）使用鈹銅模具材料，冷卻的時間可以減少40%。而模具壁溫只降低15%；以上的鈹銅模具材料的特性會給使用此材料的模具廠家帶來幾點益處成型周期縮短，生產率提高；模具壁溫均勻性好，提高拉制品的質量；模具結構簡化，因為冷卻管道減少；可以提高物料溫度，從而減小制品的壁厚，降低產品的成本。