/ DIN 17660, Kupfer-Zinn (Messinge) SS 5150, viss tillg nglighet
Cu Zn38 Pb1 German standard / DIN 17660, Kupfer-Zinn (Messinge) SS 5165, viss tillg nglighet
Cu Zn39 Pb2 Al German standard / DIN 17660, SonderMessinge SS 5253, ingen tillg nglighet
Cu Zn39 Pb2 Si German standard / DIN 17660, SonderMessinge SS 5252 (Silicon brass/Kiselm ssing),ingen tillg.
Cu Zn39 Pb3 German standard / DIN 17660, Kupfer-Zinn (Messinge) SS 5170, automatm ssing, god tillg nglighet
Cu Zn 40 Al2 German standard / DIN 17660, SonderMessinge CW713R (Cu Zn37 Mn3 Al2 Pb Si, Sonderm.)
Cu Zn40 Pb German standard / DIN 17660, Kupfer-Zinn (Messinge) SS 5163, ingen tillg nglighet
Cu Zn40 Pb2 German standard / DIN 17660, Kupfer-Zinn (Messinge) SS 5168, ingen tillg nglighet
Cu Sn4 German standard / DIN 17662, Zinnbronzen Cu Sn4
LM’s comparison list between different
在普通黃銅中加入其他合金元素所組成的多元合金稱為特殊黃銅。常加入的元素有鉛、錫、 鋁等，相應地可稱為鉛黃銅 、錫黃銅、鋁黃銅。加合金元素的目的。主要是提高抗拉強度改善工藝性。
代號︰為“ H +主加元素符號（除鋅外）+銅的質量分數+主加元素質量分數+其他元素質量分數”表示。
如︰ HPb59-1 表示銅的質量分數為 59% ，含主加元素鉛的質量分數為 1% ，余量為鋅的鉛黃銅。
青銅是金屬冶鑄史上zui早的合金，在純銅（紫銅）中加入錫或鉛的合金，有特殊重要性和歷史意義，與純銅（紫銅）相比，青銅強度高且熔點低（25%的錫冶煉青銅，熔點就會降低到800℃。純銅（紫銅）的熔點為1083℃）。青銅鑄造性好，耐磨且化學性質穩定。
青銅發明後，立刻盛行起來，從此人類歷史也就進入新的階段——青銅時代。
2015年3月28日，河南省周口市發現一處戰國至東漢時期的墓葬群，發掘出土一批精美隨葬品，其中的一把青銅劍，保存完好，十分罕見。1965年在湖北省江陵縣望山1號墓出土一把越王勾踐劍，這把寶劍穿越了兩千多年的歷史長河，劍身不見絲毫銹斑，依舊寒光閃閃、鋒利無比，被譽為“天下di1劍”