純銅是玫瑰紅色金屬，表面形成氧化銅膜後呈紫色，故工業純銅常稱紫銅或電解銅。密度為8-9g/cm2，熔點1083°C。純銅導電性很好，大量用于制造電線、電纜、電刷等；導熱性好，常用來制造須防磁性干擾的磁學儀器、儀表，如羅盤、航空儀表等；塑性很好，易于熱壓和冷壓力加工，可制成管、棒、線、條、帶、板、箔等銅材。純銅產品有冶煉品及加工品兩種。 

EFTEC3 EFTEC45 EFCUBE820 EFTEC820 EFTE98S EFTEC97 NKB032 WNS7 NKT180 BeCu11鈹銅 AGCUR MSP-1 HCL194 TAMAC194 TAMAC4 S-CUR SNDC EFTEC3 MZC1R-H C151-R440 C18140R-SH MAX375-EH STOL94-R800 C7035R-TM06 NKE010 CA725 CA720 CA690 CA694  CA688 CA687 CA675 CA670 CA704 CA857 CA908 CA863 CA774 CA715 CA360 CA353 CA356 CA350 CA345 CA342 C1975 C197 C195  SLF-10 CA155 PBP-3 PBP-2 PBP-1 

TZr0.15 TCr4.5-2.5-0.6 TCr1-0.15 TCr1-0.18 TCr0.8 TCr0.7 TCr0.5-0.1 TCr0.3-0.3 

CA145-H02 Cu-ETP-3/4H Cu-ETP-1/2H Cu-ETP-1/4H Cu-ETP-H10 Cu-ETP-H08 Cu-ETP-H06 Cu-ETP-H04 Cu-ETP-H03 Cu-ETP-H01 Cu-ETP-H02 CA110-3/4H CA110-1/2H CA110-1/4H CA110-H10 CA110-H08 CA110-H06 CA110-H04 CA110-H03 CA110-H01 CA110-H02 CA110-O60 CDA110-3/4H CDA110-1/2H CDA110-H10 CDA110-1/4H CDA110-H08 CDA110-H06 CDA110-H04 CDA110-H03 CDA110-H01 CDA110-H02 CDA110-O60 ASTM-B187 CDA110 ASTM-B187 CA110 ASTM-B187 C110 ASTM-B187 C11000 C10200-H08 C10200-H10 C10200-H06 C10200-H03 C10200-H01 C102-3/4H C102-1/2H C102-H10 C102-H08 C102-H06 C102-H04 C102-H03 C102-H01

概述

含鋁量一般不超過11.5%，有時還加入適量的鐵、鎳、錳等元素，以進一步改善性能。鋁青銅可熱處理強化，其強度比錫青銅高，抗高溫氧化性也較好。

有較高的強度 良好的耐磨性 用于強度比較高的螺桿、螺帽、銅套、密封環等，和耐磨的零部件,zui突出的特點就是其良好的耐磨性。

為含有鐵、錳元素的鋁青銅有高的強度和耐磨性，經淬火、回火後可提高硬度，有較好的高溫耐蝕性和抗氧化性在大氣、淡水和海水中抗蝕性很好，可切削性尚可，可焊接不易　焊，熱態下壓力加工良好。我國已能量產。

性能

鋁青銅具有許多優良的性能。鋁青銅具有很高的強度、硬度和耐磨性，常用來制造齒輪坯料、螺紋等零件。鋁青銅具有很好的抗蝕性，因此可用來制造耐腐蝕零件，如螺旋槳、閥門等。